Standard durability - Low gloss
Carboxyl-Terminated Polyester Resins for Exterior Use
Typically cured with Triglycidyl Isocyanurates (TGIC)
Albester SilkyMatt™ 5400 / · Acid Value 18-22 mgKOH·g⁻¹ / · Viscosity Cone & Plate 5000-6200 mPa·s (200 °C) / · approx. Tg 60°C / · Baking 10 min at 200 °C / · Cures at 96:4 with TGIC · Excellent for matt coatings when dry-blended with Albester SilkyMatt™ 5900 · Suitable for GSB and Qualicoat approvals
Albester SilkyMatt™ 5900 / · Acid Value 46-52 mgKOH·g⁻¹ / · Viscosity Cone & Plate 3000-4000 mPa·s (200 °C) / · approx. Tg 67°C / · Baking 10 min at 200 °C / · Cures at 90:10 with TGIC · Excellent for matt coatings when dry-blended with Albester SilkyMatt™ 5400 · Suitable for GSB and Qualicoat approvals · Suitable for dye-sublimation with excellent film and paper detachment
Typically cured with isocyanates
Albester SilkyMatt™ 3115 / · OH Value 280-310 mgKOH·g⁻¹ (approx.) / · Acid Value 7-11 mgKOH·g⁻¹ / · Viscosity Cone & Plate 2100-3000 mPa·s (200 °C) / · Tg 50°C (approx.) / · Baking 10 min at 200 °C / · Hydroxyl functional, highly branched resin · Combines in one shot with Albester SilkyMatt™ 3225 or Albester SilkyMatt™ 3600 for low gloss finishes · These systems are recommended in dye-sublimation and automotive applications · When used by itself, the resin provides an excellent antigrafitti and solvent resistance
Albester SilkyMatt™ 3225 / · OH Value 43-53 mgKOH·g⁻¹ (approx.) / · Acid Value 4 mgKOH·g⁻¹ (max) / · Viscosity Cone & Plate 4300-5300 mPa·s (200 °C) / · Tg 57°C (approx.) / · Baking 10 min at 200 °C / · Low gloss in one shot with Albester SilkyMatt™ 3115 and non-emitting isocyanate curative · The resulting coating system offers good flexibility, impact resistance and exterior durability · Specifically designed for Dye Sublimation effect
Albester SilkyMatt™ 3600 / · OH Value 43-53 mgKOH·g⁻¹ (approx.) / · Acid Value 4 mgKOH·g⁻¹ (max) / · Viscosity Cone & Plate 6500-8000 mPa·s (200 °C) / · Tg 63°C (approx.) / · Baking 10 min at 200 °C / · Low gloss in one shot with Albester SilkyMatt™ 3115 and non-emitting isocyanate curative · The resulting coating system offers good flexibility, impact resistance and exterior durability · Specifically designed for Dye Sublimation effect · High storage stability
Standard durability - High gloss
Carboxyl-Terminated Polyester Resins for Exterior Use
Typically cured with β-hydroxy alkyl amide (β-HAA)
Albester™ 5650 / · Acid Value 30-35 mgKOH·g⁻¹ / · Viscosity Cone & Plate 1800-2800 mPa·s (200 °C) / · Tg 56°C (approx.) / · Baking 10 min at 180 °C / · Cures at 95:5 with β-HAA · The resulting coatings exhibit an excellent flow and appearance · Suitable for curing with proper Acrylic curative to achieve full matt · Suitable for GSB and Qualicoat approvals
Typically cured with Triglycidyl Isocyanurates (TGIC)
Albester™ 5148 / · Acid Value 32-38 mgKOH·g⁻¹ / · Viscosity Cone & Plate 3500-4500 mPa·s (200 °C) / · Tg 68°C (approx.) / · Baking 10 min at 200 °C / · Suitable for TGIC at 93/7 ratio · Low reactivity resin · Excellent storage stability together with an excellent flow · Exterior durable for architectural applications · Suitable for GSB and Qualicoat approvals
Albester™ 5050 / · Acid Value 32-38 mgKOH·g⁻¹ / · Viscosity Cone & Plate 3000-3800 mPa·s (200 °C) / · Tg 61°C (approx.) / · Baking 10 min at 180 °C / · Designed for combination with TGIC in 93:7 ratio or with β-HAA in 95:5 ratio · Excellent reactivity resin · Suitable for curing with proper Acrylic curative to achieve full matt
Albester™ 5070 / · Acid Value 32-37 mgKOH·g⁻¹ / · Viscosity Cone & Plate 2800-3800 mPa·s (200 °C) / · Tg 61°C (approx.) / · Baking 15 min at 150 °C / · Designed for curing with TGIC in 93:7 ratio for high speed lines · Starts curing from 130 °C · The resulting coatings exhibit, excellent flexibility and exterior durability · Designed to be used with texturing agent for wrinkle effect
Typically cured with isocyanates
Albester™ 3120 / · OH Value 45-55 mgKOH·g⁻¹ (approx.) / · Acid Value 8 mgKOH·g⁻¹ (max) / · Viscosity Cone & Plate 4800-6000 mPa·s (200 °C) / · Tg 56°C (approx.) / · Baking 10 min at 200 °C / · Designed primarily to be cured with aliphatic isocyanates · Also cured with Uretdione technology · Superior flow, excellent exterior durability, flexibility, gloss and pigment wetting · Suitable for clear coating
Albester™ 3310 / · OH Value 100-120 mgKOH·g⁻¹ (approx.) / · Acid Value 8 mgKOH·g⁻¹ (max) / · Viscosity Cone & Plate 3200-4200 mPa·s (200 °C) / · Tg 57°C (approx.) / · Baking 10 min at 200 °C / · Cured in combination with non-emitting isocyanates · Excellent solvent, detergent and stain resistance with good mechanical properties
Superdurable – Low gloss
Carboxyl-Terminated Polyester Resins for Exterior Use
Typically cured with β-hydroxy alkyl amide (β-HAA)
Albester SilkyMatt™ 6520 / · Acid Value 14-18 mgKOH·g⁻¹ / · Viscosity Cone & Plate 1800-2600 mPa·s (200 °C) / · Tg 56°C (approx.) / · Baking 15 min at 180 °C / · Cures at 97.5:2.5 · Provides very low gloss when dry-blended with Albester SilkyMatt™ 6580 · GSB Master and Qualicoat Class 2 approvals
Albester SilkyMatt™ 6590 / · Acid Value 70-80 mgKOH·g⁻¹ / · Viscosity Cone & Plate 1700-3000 mPa·s (200 °C) / · Tg 69°C (approx.) / · Baking 10 min at 180 °C / · Cures at 90:10 · Improved humidity resistances · Superdurable · Suitable for GSB Master and Qualicoat Class 2 approvals
Isocyanate curing
Albester SilkyMatt™ 6615 / · OH Value 270-300 mgKOH·g⁻¹ (approx.) / · Acid Value 6 mgKOH·g⁻¹ (max) / · Viscosity Cone & Plate 2400-3400 mPa·s (200 °C) / · Tg 53°C (approx.) / · Baking 10 min at 200 °C / · Superdurable resin · Blended in one shot with Albester SilkyMatt™ 6620 to produce low gloss finishing · Suitable for dye-sublimation · Suitable for GSB Master and Qualicoat Class 2 approvals
Superdurable – High gloss
Carboxyl-Terminated Polyester Resins for Exterior Use
Typically cured with Triglycidyl Isocyanurates (TGIC)
Albester™ 6140 / · Acid Value 30-35 mgKOH·g⁻¹ / · Viscosity Cone & Plate 4000-6000 mPa·s (200 °C) / · Tg 65°C (approx.) / · Baking 10 min at 200 °C / · Designed to give a superior exterior durability in 93:7 ratio with TGIC · Suitable for GSB and Qualicoat Class 2 approvals
Emulsion for roof tile coatings
Acrylic emulsion
Plextol PR3500 / · Viscosity 200 mPa·s / · Tg 16°C (approx.) / · Very fine particle size · Free of solvents and plasticizers / · Specially designed for penetration into porous substrates · Excellent consolidation power
Carboxyl-Terminated Polyester Resins for Interior Use
Typically cured with epoxy resins
50/50 Mixing
Albester™ 2380 / · Acid Value 68-78 mgKOH·g⁻¹ / · Viscosity Cone & Plate 1800-3000 mPa·s (200 °C) / · Tg 57°C (approx.) / · Baking 15 min at 160 °C / · In combination with suitable epoxy resin in 50:50 ratio · Typical resin for Domestic Appliance when excellent chemical properties are required
60/40 Mixing
Albester™ 2100 / · Acid Value 47-53 mgKOH·g⁻¹ / · Viscosity Cone & Plate 2000-2800 mPa·s (200 °C) / · Tg 53°C (approx.) / · Baking 15 min at 200 °C / · Low reactivity resin for 60:40 hybrid coatings · Offers outstanding flow in combination with suitable epoxy resins · Suitable as Primer on metal substrates · Can be applied in the transportation field
Albester™ 2230 / · Acid Value 47-53 mgKOH·g⁻¹ / · Viscosity Cone & Plate 1800-2600 mPa·s (200 °C) / · Tg 53°C (approx.) / · Baking 10 min at 180 °C / · High reactivity resin for hybrid coatings in combination with suitable epoxy resins in 60:40 ratio · Perfect resin for thin film applications and high quality for Domestic Appliance coatings
Albester™ 2758 / · Acid Value 48-55 mgKOH·g⁻¹ / · Viscosity Cone & Plate 1800-3500 mPa·s (200 °C) / · Tg 61°C (approx.) / · Baking 10 min at 180 °C / · In combination with suitable epoxy resins in 60:40 ratio for hybrid coatings · High Tg along with excellent storage stability